Grain Direction Aluminum Sheet

By default in my testing the bounding box aligns itself with the longest straight side.

Grain direction aluminum sheet.

A plate s grains run parallel to the rolling direction. The long tranverse lt the short transverse st and the longitudinal l. As a general rule the grain line must run perpendicular to the bend to avoid the potential for cracking or fracture. Bending with the grain gives a different result than bending against it.

You must pay careful attention to grain or rolling direction when bending high strength metals especially when trying to achieve a small inside bend radius. The software determines the smallest rectangle bounding box that aligns with the grain direction to fit the flat pattern. Applying this to metal bending be it plate bending press braking or any other type of metal forming consideration must be given to the grain direction before any process is carried out. From mil hdbk 5 7075 t62 2 501 3 000 thick stock ultimate tension allowable stress is l 67 ksi lt 70 ksi and st 66 ksi.

The grain direction is established during the metal rolling process. From the flat pattern properties we can select a new edge for the grain direction. Whereas bending parallel to rolling direction can lead to cracks because of destruction in grain structure. That has negligible impact on part strength.

Bending with the grain or parallel to the grain direction can be a contributor to material failure as bending along the grain allows for separation of the grain boundaries. Aluminum plate thickness gt 250 inch has three grain orientations each with their own strength values. You can define a grain direction to use when calculating the bounding box for sheet metal parts. The grain direction is in the rolling direction of the sheet as it was being manufactured.

Bending metal against the grain or perpendicular to the grain is a common way to prevent material failure or cracking. The three orientations are. During sheet metal processing rolling operation material grains are arranged in the direction of rolling. Two rollers compressing the hot metal cause the polycrystalline material to elongate in the direction of rolling.

You ll now see that your flat pattern is generated based on one edge oriented parallel to the angled edge and the other obviously perpendicular to that in drawing the rectangle.